Growth, microstructure, and failure of crazes in glassy polymers

TitleGrowth, microstructure, and failure of crazes in glassy polymers
Publication TypeJournal Article
Year of Publication2003
AuthorsRottler, Jörg, and Mark O. Robbins
JournalPhysical Review E
Volume68
Pagination011801
Date Publishedjul
AbstractWe report on an extensive study of craze formation in glassy polymers. Molecular dynamics simulations of a coarse-grained bead-spring model were employed to investigate the molecular level processes during craze nucleation, widening, and breakdown for a wide range of temperature, polymer chain length N, entanglement length Ne, and strength of adhesive interactions between polymer chains. Craze widening proceeds via a fibril-drawing process at constant drawing stress. The extension ratio is determined by the entanglement length, and the characteristic length of stretched chain segments in the polymer craze is Ne/3. In the craze, tension is mostly carried by the covalent backbone bonds, and the force distribution develops an exponential tail at large tensile forces. The failure mode of crazes changes from disentanglement to scission for {N/Ne∼10}, and breakdown through scission is governed by large stress fluctuations. The simulations also reveal inconsistencies with previous theoretical models of craze widening, which were based on continuum level hydrodynamics.
URLhttp://link.aps.org/doi/10.1103/PhysRevE.68.011801
DOI10.1103/PhysRevE.68.011801
Website development by Checkmark Media. Designed by Armada.

a place of mind, The University of British Columbia

Faculty of Science
Department of Physics and Astronomy
6224 Agricultural Road
Vancouver, BC V6T 1Z1
Tel 604.822.3853
Fax 604.822.5324

Emergency Procedures | Accessibility | Contact UBC | © Copyright The University of British Columbia